Gilding

Very good resistance to wear, used on connections. Gold - Cobalt alloy, 99.5% of gold.

 
Coating thickness 0.02 to 5 μm
Excess thickness caused by the deposit Same as thickness deposited
Hardness 120 – 180 Hv
Conductivity Very good
Weldability Weldable
Salt spray test resistance 168 h according to ISO 9227 and ASTM B 117 standards
Paint adhesion Not applicable
Slip No
Appearance Glossy orangish yellow
Substrate Steel, Stainless steel
Copper or Brass with nickel undercoat
Aluminium with nickel undercoat
Capacity Length Width Height
600 mm 400 mm 600 mm
Treatment techniques Single, frame or barrel
Comments Very good resistance to wear.
Used for connections.